FerroManganese
Size:1-100mm
Basic Info：
| Ferromanganese International Brand | ||||||||
|
category |
Brand name |
chemical composition（wt%） |
||||||
|
Mn |
C |
Si |
P |
S |
||||
|
Ⅰ |
Ⅱ |
Ⅰ |
Ⅱ |
|||||
|
Range |
≤ |
|||||||
|
Low carbon ferromanganese |
FeMn82C0.2 |
85.0—92.0 |
0.2 |
1.0 |
2.0 |
0.10 |
0.30 |
0.02 |
|
FeMn84C0.4 |
80.0—87.0 |
0.4 |
1.0 |
2.0 |
0.15 |
0.30 |
0.02 |
|
|
FeMn84C0.7 |
80.0—87.0 |
0.7 |
1.0 |
2.0 |
0.20 |
0.30 |
0.02 |
|
|
category |
Brand name |
chemical composition（wt%） |
||||||
|
Mn |
C |
Si |
P |
S |
||||
|
Ⅰ |
Ⅱ |
Ⅰ |
Ⅱ |
|||||
|
Range |
≤ |
|||||||
|
Medium carbon ferromanganese |
FeMn82C1.0 |
78.0—85.0 |
1.0 |
1.5 |
2.0 |
0.20 |
0.35 |
0.03 |
|
FeMn82C1.5 |
78.0—85.0 |
1.5 |
1.5 |
2.0 |
0.20 |
0.35 |
0.03 |
|
|
FeMn78C2.0 |
75.0—82.0 |
2.0 |
1.5 |
2.5 |
0.20 |
0.40 |
0.03 |
|
|
category |
Brand name |
chemical composition（wt%） |
||||||
|
Mn |
C |
Si |
P |
S |
||||
|
Ⅰ |
Ⅱ |
Ⅰ |
Ⅱ |
|||||
|
Range |
≤ |
|||||||
|
High carbon ferromanganese |
FeMn78C8.0 |
75.0—82.0 |
8.0 |
1.5 |
2.5 |
0.20 |
0.33 |
0.03 |
|
FeMn74C7.5 |
70.0—77.0 |
7.5 |
2.0 |
3.0 |
0.25 |
0.38 |
0.03 |
|
|
FeMn68C7.0 |
65.0—72.0 |
7.0 |
2.5 |
4.5 |
0.25 |
0.40 |
0.03 |
|
Ferromanganese is a kind of ferroalloy that is composed of iron and manganese.is made by heating a mixture of the oxides MnO2 and Fe2O3, with carbon, usually as coal and coke, in either a blast furnace or an electric arc furnace-type system, called a submerged arc furnace. The oxides undergo carbothermal reduction in the furnaces, producing the ferromanganese.
It can be divided into High carbon ferromanganese/HCFeMn(C:7.0%-8.0%),Medium carbon ferromanganese/MCFeMn:(C:1.0-2.0%),and Low carbon ferromanganese/LCFeMn(C<0.7%). it is available in a wide range of sizes .
Ferromanganese production takes manganese ore as raw material and lime as auxiliary material,uses electric furnace to smelt.
Application:
①Ferromanganese performs well in steel-making,it is deoxidizer and alloying constituent,and meanwhile can reduce sulfur content and damage caused by sulfur.
②Liquid ateel mixed by ferromanganese can improve mechanical properties od steel with high strength,toughness,wear resistance,ductility,ect.
③Ferromanganese is a very important auxiliary material in steel-making and iron casting industries.